Description
The KRATIR MII PA6 CF7 filament is a high-performance material designed for demanding industrial applications. Crafted from polyamide 6 (PA6) reinforced with 7% carbon fiber, it offers enhanced mechanical properties, including increased stiffness, strength, and thermal stability. This makes it ideal for producing durable, lightweight parts that require high dimensional accuracy and resistance to wear and heat.
Compatible with most FDM/FFF 3D printers, the KRATIR PA6 CF7 filament is suitable for applications in automotive, aerospace, and engineering sectors.
| Property | Method | Units | Value |
|---|---|---|---|
| Filament diameter (+/- 0.05 mm) | mm | 1.73 | |
| Density | ISO 1183-1 | g/cm3 | 1.18 |
| Humidity absorbtion (70 °C, 62% r.H.)* | ISO 1110 | % | |
| Water absorbtion (23 °C saturated)* | ISO 62 | % |
KRATIR MII PA6 CF - Plug & Play in Continuous Fiber Systems
Inspired by the solid and unwavering nature of stone
Mechanical Properties
| Property | Method | Units | Value XZ** (on edge) | Value ZX** (upright) |
|---|---|---|---|---|
| Tensile Modulus | ISO 527 Type 1BA | MPa | 5800 | 2000 |
| Tensile Strength at yield | ISO 527 Type 1BA | MPa | 112 | 45 |
| Tensile Strength at break | ISO 527 Type 1BA | MPa | - | - |
| Elongation at yield | ISO 527 Type 1BA | % | 3.9 | 4.9 |
| Elongation at break | ISO 527 Type 1BA | % | 7.1 | 5.0 |
| Flexural Modulus | ISO 178 | MPa | ||
| Flexural Strain at break | ISO 178 | % |
Thermal Properties
| Property | Method | Units | Value |
|---|---|---|---|
| Glass transition temperature (Tg) | ISO 11357-1 | °C | 60 |
| Melting temperature | ISO 11357-3 | °C | 220 |
| Vicat softening temperature | ISO 306/B50 | °C | |
| Temp. of deflection under load (1.80 MPa)* | ISO 75-1/-2 | °C | 180 |
| Temp of deflection under load (0.45 MPa)* | ISO 75-1/-2 | °C |
Recommended Processing Conditions
| Nozzle Temperature | Recommended 280°C (280°C - 310°C) |
| Bed Temperature | Recommended 110°C (80°C - 120°C) |
| Chamber Temperature | Recommended 90°C (23°C - 90°C) |
| Bed Material | (Textured) PEI Sheet, Glass, Carbon Fibre Plate |
| Adhesion Promoter | Magigoo PA or Magigoo HT |
| Nozzle Diameter, hardened steel nozzle | >= 0.6mm |
| Print Speed | Recommended: 30mm/s (30-50 mm/s) |
| Drying Instructions | 100°c for 4 - 6 hours |