HighTemp DL401 is a rigid resin designed for moulding applications, possessing both high stiffness and ductility, and capable of withstanding high temperatures. Parts created in DL401 show superior compression behaviour, and resistance to fatigue, temperature, and moisture without bending or deforming. HighTemp DL401 can be used for quick printing applications and can print with an impressive layer thickness of 350 microns.
Best Used for:
• Hot fluid and gas manifolds
• Moulds and inserts
• Heat resistant housings and fixtures
• Outdoor applications
Unique Features:
• Excellent long-lasting performance under heat and stress
• Quick and fast prototyping 350 μm layer
• Simulating the strength and stiffness of glass filled Nylon 6
• Smooth surface finish and ability to print fine details
• Minimal shrinkage. dry surface touch
• Ideal for plastic injection moulding
Compatible Printers:
LC Magna and LC Titan
| Tensile Properties | ||
|---|---|---|
| Tensile Modulus * | 3180 MPa | ASTM D638 |
| Ultimate Tensile Strength * | 76.9 MPa | ASTM D638 |
| Elongation at break * | 4.8% | ASTM D638 |
| Flexural Properties | ||
| Flexural Strength * | 123 MPa | ASTM D790 |
| Flexural Modulus * | 3240 MPa | ASTM D790 |
| Impact Properties | ||
| Impact Strength Notched Izod * | 15.8 J/m | ASTM D256 |
| General Properties | ||
| Hardness * | 92 Shore D | ASTM D2240 |
| Water Absorption (Short Term) * | 0.28% | ASTM D570 |
| Viscosity | 700 cPs | At 25°C Brookfield spindle 3 |
| Density | 1.10 g/cm3 | |
| Storage | Between 10 and 50°C | |
| Colour | Amber | |
*Mechanical properties stated based on fully cured material.