Incredibly versatile resin Durable DL110H can handle impact, compression, bending and stress fatigue without breaking or deforming.
Best Used for:• Jigs and fixtures requiring minimal deflection at elevated temperature like drill holder, air intake
• Cover-plates and enclosures like automotive and motorsport interior
• Fastenings, tools & couplings
• Strong and stiff prototype
Compatible Printers:
LC Magna & LC Titan (Not suitable for UV 3D Printers)
Note: DL110HW White variation not compatible with LC Titan
USPs:• Heat Deflection Temperature 80 °C
• High impact strength
• Tough, Durable, and long lasting
• Simulating the strength and stiffness of ABS
• High definition and can hold fine details
• Smooth surface finish
| Tensile Properties | ||
|---|---|---|
| Tensile Modulus * | 2100 MPa | ASTM D638 |
| Ultimate Tensile Strength * | 60 MPa | ASTM D638 |
| Elongation at break * | 14% | ASTM D638 |
| Flexural Properties | ||
| Flexural Strength * | 81 MPa | ASTM D790 |
| Impact Properties | ||
| Impact Strength Notched Izod * | 110 J/m | ASTM D256 |
| General Properties | ||
| Hardness * | 85 Shore D | ASTM D2240 |
| Heat Deflection Temperature * | 80°C | ASTM D648 |
| Water Absorption (Short Term) | 1.06% | ASTM D570 |
| Viscosity | 480 cPs | At 25°C Brookfield spindle 3 |
| Density | 1.14 g/cm3 | |
| Storage | Between 10°C and 50°C | |
| Colours | Black, White, Smokey Quartz Translucent | |
* Post cured for 2 hours at 60°C with Photocentric Cure L2