The 3D filament Kimya PLA-R is a recycled and biodegradable polymer: this biosourced homopolymer can be obtained from corn starch. Polylactic acid (PLA) is a natural alternative to polyethylene. It is easy to print and...
Call our expert advisors to get a tailored solution on 01257 228411 or add this product for a personalised quote
The 3D filament Kimya PLA-R is a recycled and biodegradable polymer: this biosourced homopolymer can be obtained from corn starch. Polylactic acid (PLA) is a natural alternative to polyethylene. It is easy to print and is odorless. The 3D filament Kimya PLA-R can be used in industrial applications, notably packaging, and also in domestic applications: creation of everyday objects, toys, prototypes and for use in modeling. It offers the following properties:
PROPERTIES | TEST METHODS | VALUES |
---|---|---|
Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
Density | ISO 1183-1 | 1.24 g/cm3 |
Moisture rate | INS-6711 | < 1 % |
Melt flow index (MFI) | ISO 1133-1 (@210°C“ 2,16 kg) | 9 - 12 g/10min |
Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-220°C) | 61 °C |
Melting Temperature (Tm) | ISO 11357-1 DSC (10°C/min“ 20-220°C) | 150 °C |
PRINTING DIRECTION | XY |
---|---|
Printing Speed | 40-150 mm/s |
Infill | 100% - rectilinear |
Infill Angle | 45°/-45° |
Nozzle Temperature | 190-210°C |
Bed T° | 20-60°C |
PROPERTIES | TEST METHODS | VALUES | |
---|---|---|---|
MECHANICAL PROPERTIES | |||
Tensile modulus | ISO 527-2/5A/50 | 2,963 MPa | |
Tensile Strength | ISO 527-2/5A/50 | 57.9 MPa | |
Tensile strain at strength | ISO 527-2/5A/50 | 2.2 % | |
Tensile Stress at Break | ISO 527-2/5A/50 | 47.3 MPa | |
Tensile strain at break | ISO 527-2/5A/50 | 4 % | |
Flexural modulus | ISO 178 | 2,675 MPa | |
Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 88.8 MPa | |
Flexural stress at break | ISO 178 | 91.6 MPa | |
Charpy impact resistance | ISO 179-1/1eA | 3.22 kJ/m² | |
Shore Hardness | ISO 868 | 79.1D |
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.
Spool Material | PC |
Steaming Temperature | 65°C |
Steaming Duration | 2h-4h |