Kimya PETG-R ("R for recycled") 3D filament is formulated based on industrial waste from a luxury and medical packaging company. Recycled, but equally powerful, it has similar technical properties to the PETG-S ("S for standard") filament.
- Contains at least 95% post-industrial recycled materials for the non-translucent coloured version (100% for the translucent natural version)*.
- Similar mechanical properties to PETG-S
- Odorless
- Easy printing
- 100% recycled material from France
Recommended Print Settings
Print speed: 40 - 70 mm/s
Print nozzle temperature: 195 - 230 °C
Print bed temperature: 35 - 60 °C
*Note Due to the use of recycled material, slight colour variations may occur between production batches. This does not affect the technical characteristics of the product, which are systematically checked by Kimya's quality team.
Technical Specifications
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.27 g/cm3 |
| Melt flow index (MFI) | ISO 1133-1 (@225°C €“ 2.16 kg) | 9.2 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-300°C) | 80 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 30 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 0°/0° |
| Nozzle Temperature | 245°C |
| Bed T° | 80°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/1A/50 | 1,845 MPa |
| Tensile Strength | ISO 527-2/1A/50 | 47.1 MPa | |
| Tensile strain at strength | ISO 527-2/1A/50 | 3.8 % | |
| Tensile Stress at Break | ISO 527-2/1A/50 | 37.2 MPa | |
| Tensile strain at break (type A) | ISO 527-2/5A/50 | 3.6-13 % | |
| Flexural modulus | ISO 178 | 1,746 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 60.8 MPa | |
| Charpy impact resistance | ISO 179-1/1eA | 6.1 kJ/m² | |
| Shore Hardness | ISO 868 | 75.5D |
3D Printing Profiles
PRINT SETTINGS:
- PRINT SPEED : 40-70 mm/s
- EXTRUSION TEMPERATURE : 195-230°C
- PLATFORM TEMPERATURE : 35-60°C
MISCELLANEOUS
| Spool Material | PC |
| Steaming Temperature | 65°C |
| Steaming Duration | 2h-4h |