The Kimya PEI-9085 3D filament belongs to the family of thermoplastic polyimides. Polyetherimide (PEI) is an amorphous thermoplastic. If benefits from good resistance to temperature, high resistance to abrasion and high dimensional stability. It is...
Call our expert advisors to get a tailored solution on 01257 228411 or add this product for a personalised quote
The Kimya PEI-9085 3D filament belongs to the family of thermoplastic polyimides. Polyetherimide (PEI) is an amorphous thermoplastic. If benefits from good resistance to temperature, high resistance to abrasion and high dimensional stability. It is used in sectors such as aerospace, railway, electronics and transport etc. The Kimya PEI-9085 3D filament has the following properties:
PROPERTIES | TEST METHODS | VALUES |
---|---|---|
Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
Density | ISO 1183-1 | 1.34 g/cm3 |
Moisture rate | INS-6711 | < 1 % |
Heat distortion temperature (HDT) (1.8 MPa) | ASTM D648 | 153°C |
Melting Temperature (Tm) | DSC | 0 °C |
PRINTING DIRECTION | XY |
---|---|
Printing Speed | 20-35 mm/s |
Infill Angle | 45°/-45° |
Nozzle Temperature | 350-380°C |
Bed T° | 140-170°C |
PROPERTIES | TEST METHODS | VALUES | |
---|---|---|---|
MECHANICAL PROPERTIES | |||
Tensile modulus | ASTM D738 | 3,440 MPa | |
Tensile Stress at Break | ASTM D738 | 74 MPa | |
Tensile strain at break | ASTM D738 | 72 % | |
Flexural modulus | ASTM 790 | 2,920 MPa | |
Charpy impact resistance | ISO 179/2C | 11 kJ/m² |
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.
Spool Material | PC |
Steaming Temperature | 120°C |
Steaming Duration | 4h-6h |