Description
Technical filament from polyamide modified for 3D-printing in FFF with additional carbon fibers. The carbon fibers reduce the shrinkage and the warping behaviour extremely.
Material Properties
Material shows superior strength with remaining impact resistance. Recommended for all high-strength parts with good heat- and media resistance.
- Printed parts show an attractive matte surface finish.
- Printed parts with thin wall layers can become very flexible under high humidity intake - in this case we recommend F3 PA-CF Lite.
- The material differs from F3 PA-CF Lite in higher tensile strength, better printability and more sensitivity towards moisture.
- The stiffness of the filament should be considered for the pipes and the feeder system of the printer to avoid breaking.
Technical Information
Mechanical properties
Density | g/ cm³ | 1,25 |
Modulus of Elasticity printed specimen | MPa (N/mm²) | 14400 |
Tensile strength printed specimen x-y (+ 45°/-45°) | MPa (N/mm²) | 85 |
Tensile strength printed specimen x-y (0°) | MPa (N/mm²) | 120 |
Tensile strength printed specimen x-y (90°) | MPa (N/mm²) | 40 |
Tensile stress printed specimen x-y (0°) | MPa (N/mm²) | 112,73 |
Elongation printed specimen (0°) | % | 0,98 |
Flexural modulus printed specimen (+ 45°/-45°) | GPa (kN/mm²) | 4,78 |
Impact strength printed specimen x-y (+ 45°/-45°)(Charpy) | kJ/m² | 47 |
Shore hardness | --- | -- |
Thermal properties
Glass transition temp. | °C | 68 |
Heat distortion temp. | (HDT) °C | 120 |
Data Sheets
Printers
The Material has been tested on following printers:
Printer | F3 PA-CF Pro | F3 PA-GF Pro | F3 PA Pure Pro | F3 PA-CF Lite | F3 PA Pure Pro |
3NTR A2/A4 | x | x | x | x | x |
Evo-Tech Evolizer EL-102 | x | x | x | x | x |
Hage3D 84L/140L | x | x | x | x | x |
Multec M500/M800 | x | x | x | x | x |
Prusa I3 MK3S | x | x | x | ||
Raise3D N2/N2+ (Bondtech-upgrade) | x | x | x | x | x |
Raise3D Pro2/Pro2+ | x | x | x | ||
Ultimaker S5/S3 | x | x | x | x | x |
Zortrax M200 Plus | x | x |