Description
The 3D filament Kimya ABS Kevlar belongs to the styrenic polymer family. Acrylonitrile-butadiene-styrene-Kevlar (ABS Kevlar) is a mixture of ABS and aramid fibers. It offers superior properties to a standard ABS. It offers the printed parts a higher level of resistance to abrasion and impact. It must be stored in dry conditions at ambient temperature for optimum conservation and utilization. It is used for finished parts and tools. The 3D filament Kimya ABS Kevlar has the following properties:
- No shrinkage
- Low wrapping
- Smooth surface
- Light weight objects
Technical Information
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.032 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@220°C 10 kg) | 35.7 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-220°C) | 100 °C |
| Melting Temperature (Tm) | ISO 11357-1 DSC (10°C/min - 20-220°C) | 30 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 50 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 260°C |
| Bed T° | 100°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | |||
| Tensile modulus | ISO 527-2/5A/50 | 1,775 MPa | |
| Tensile Strength | ISO 527-2/5A/50 | 31.1 MPa | |
| Tensile strain at strength | ISO 527-2/1A/50 | 2 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 27.7 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 4 % | |
| Flexural modulus | ISO 178 | 1,509 MPa | |
| Flexural strength* | ISO 178 | > 5 % | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 44.7 MPa | |
| Charpy impact resistance | ISO 179-1/1eA | 8 kJ/m² | |
| Shore Hardness | ISO 868 | 65,2D |
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.
Print Setting
Miscellaneous
| Spool Material | PC |
|---|---|
| Steaming Temperature | 120°C |
| Steaming Duration | 4h-6h |