KRATIR PA11 CF is a high-performance 3D printing filament that seamlessly combines strength, sustainability, and precision. Crafted by Tectonic-3D, this material is engineered for professionals seeking top-tier mechanical properties and eco-conscious design.
| Property | Method | Units | Value |
|---|---|---|---|
| Filament diameter (+/- 0.05 mm) | mm | 1.75/2.85 | |
| Density | ISO 1183-1 | g/cm3 | 1.13 |
| Humidity absorbtion (70 °C, 62% r.H.)* | ISO 1110 | % | 0.7 - 0.9 |
| Water absorbtion (23 °C saturated)* | ISO 62 | % | 1.3 - 1.7 |
KRATIR PA11 CF - High Strength & Part Repeatability
Inspired by the solid and unwavering nature of stone
KRATIR PA11 CF derives its name from mythology and the elemental essence of earth and stone, symbolizing strength and stability. The name "KRATIR" also draws its etymological inspiration from the ancient Greek word "κρατήρ" (pronounced "kratír"), which refers to a large, shallow bowl or vessel often used for mixing during ancient Greek rituals and ceremonies. The resulting remarkable blend, has 97% bio-based polyamide sourced from castor oil and infused with recycled carbon fiber.
| Property | Method | Units | Value XZ** (on edge) | Value ZX** (upright) |
|---|---|---|---|---|
| Tensile Modulus | ISO 527 Type 1BA | MPa | 8900 | 1400 |
| Tensile Strength at yield | ISO 527 Type 1BA | MPa | no yield | no yield |
| Tensile Strength at break | ISO 527 Type 1BA | MPa | 105 | 34 |
| Elongation at yield | ISO 527 Type 1BA | % | no yield | no yield |
| Elongation at break | ISO 527 Type 1BA | % | 4.5 | 10.8 |
| Flexural Modulus | ISO 178 | MPa | 8098 | 1471 |
| Flexural Stress at break | ISO 178 | % | 70 | 35 |
| Flexural Strain at break | ISO 178 | % | 1.3 | 1.3 |
| Property | Method | Units | Value |
|---|---|---|---|
| Glass transition temperature (Tg) | ISO 11357-1 | °C | |
| Melting temperature | ISO 11357-3 | °C | 189 |
| Vicat softening temperature | ISO 306/B50 | °C | |
| Temp. of deflection under load (1.80 MPa)* | ISO 75-1/-2 | °C | 180 |
| Temp of deflection under load (0.45 MPa)* | ISO 75-1/-2 | °C |
| Nozzle Temperaure | Recommended 285°C (260°C - 290°C) |
| Bed Temperature | Recommended 110°C (90°C - 110°C) |
| Chamber Temperature | Recommended 90°C (23°C - 90°C) |
| Bed Material | (Textured) PEI Sheet, Glass, Carbon Fibre Plate |
| Adhesion Promoter | Magigoo PA |
| Nozzle Diameter | >= 0.4mm, hardened steel nozzle |
| Print Speed | Recommended: 30mm/s (30-100 mm/s) |
| Max. Volumetric Speed (high speed) | 16mm3/s (150mm/s) |
| Drying Instructions | 120°c for 6 - 8 hours |