FILAMENT PROPERTIES
| PROPERTIES |
TEST METHODS |
VALUES |
| Diameter |
INS-6712 |
1.75 ± 0.1 mm |
| Density |
ISO 1183-1 |
1.03 g/cm3 |
| Moisture rate |
INS-6711 |
< 1 % |
| Melt flow index (MFI) |
ISO 1133-1 (@220°C 10 kg) |
4.7 - 7.1 g/10min |
| Glass transition temperature (Tg) |
ISO 11357-1 DSC (10°C/min - 20-300°C) |
97 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION |
XY |
| Printing Speed |
20-70 mm/s |
| Infill |
100% - rectilinear |
| Infill Angle |
45°/-45° |
| Nozzle Temperature |
250-290°C |
| Bed T° |
60-100°C |
PRINTED SPECIMENS PROPERTIES
|
PROPERTIES |
TEST METHODS |
VALUES |
| MECHANICAL PROPERTIES |
| Tensile modulus |
ISO 527-2/5A/50 |
1,273 MPa |
| Tensile Strength |
ISO 527-2/5A/50 |
23.7 MPa |
| Tensile strain at strength |
ISO 527-2/5A/50 |
1 % |
| Tensile Stress at Break |
ISO 527-2/5A/50 |
16.7 MPa |
| Tensile strain at break |
ISO 527-2/5A/50 |
11 % |
| Flexural modulus |
ISO 178 |
1,533 MPa |
| Flexural stress at conventional deflection (3,5% strain)* |
ISO 178 |
36.2 MPa |
| Charpy impact resistance |
ISO 179-1/1eA |
7 kJ/m² |
| Shore Hardness |
ISO 868 |
76,6D |
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.