The 3D filament Kimya TPC-91A belongs to the family of copolyester thermoplastic elastomers. Thermoplastic copolyester (TPC) is produced by copolymerizing two types of monomers: an elastomer and a plastic. TPC offers chemical and impact resistance. It provides Shore hardness of 91 A. It can be used to produce flexible and elastic parts. The 3D filament Kimya TPC-91A can be used in industrial applications in sectors such as electronics, textiles, roofing, etc., and in decorative and leisure 3D printing applications. It offers the following properties:
FILAMENT PROPERTIES
PROPERTIES | TEST METHODS | VALUES |
---|---|---|
Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
Density | ISO 1183-1 | 1.22 g/cm3 |
Moisture rate | INS-6711 | < 1 % |
Melt flow index (MFI) | ISO 1133-1 (@210°C 2,16 kg) | 18 - 20 g/10min |
Melting Temperature (Tm) | ISO 11357-1 DSC (10°C/min 20-220°C) | 160 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
PRINTING DIRECTION | XY |
---|---|
Printing Speed | 44 mm/s |
Infill | 100% - rectilinear |
Infill Angle | 45°/-45° |
Nozzle Temperature | 260°C |
Bed T° | 60°C |
PRINTED SPECIMENS PROPERTIES
PROPERTIES | TEST METHODS | VALUES | |
---|---|---|---|
MECHANICAL PROPERTIES | |||
Tensile modulus | ISO 37/2/500 | 67 MPa | |
Tensile Strength | ISO 37/2/500 | 17.7 MPa | |
Tensile strain at strength | ISO 37/2/500 | 0 % | |
Tensile Stress at Break | ISO 37/2/500 | 17.5 MPa | |
Tensile strain at break | ISO 37/2/500 | 0 % | |
Flexural modulus | ISO 178 | 66 MPa | |
Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 2.6 MPa | |
Charpy impact resistance | ISO 179-1/1eA | No Break | |
Shore Hardness | ISO 868 | 91A |
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.
Data Sheets
Description | Le filament flexible Kimya de la famille des ©lastom¨res thermoplastiques copolyesters. |
---|---|
Highlight | Flexibility |
Highlight 2 | Easy To Print |
Highlight 3 | Lengthening> 500% |
Spool Material | PC |
Steaming Temperature | 120°C |
Steaming Duration | 4h-6h |