Description
Technical filament from polyamide modified for 3D-printing in FFF with additional carbon fibers.
Material Properties
- The carbon fibers reduce the shrinkage and the warping behaviour extremely. Material shows excellent strength with remaining impact resistance.
- Recommended for all parts with good heat- and media resistance where light weight or high strength matters.
- Printed parts show an excellent matte surface finish.
- The material differs in the print process from F3 PA-CF Pro in reduced moisture sensitivity and need for much more heat intake in the hotend for proper layer adhesion.
- The stiffness of the filament should be considered for the pipes and the feeder system of the printer to avoid breaking.
Technical Information
Mechanical properties
| Density | g/ cm³ | 1,24 |
| Modulus of Elasticity printed specimen | MPa (N/mm²) | 11500 |
| Tensile strength printed specimen x-y (+ 45°/-45°) | MPa (N/mm²) | 65 |
| Tensile strength printed specimen x-y (0°) | MPa (N/mm²) | 90 |
| Tensile strength printed specimen x-y (90°) | MPa (N/mm²) | 30 |
| Tensile stress printed specimen x-y (0°) | MPa (N/mm²) | -- |
| Elongation printed specimen (0°) | % | -- |
| Flexural modulus printed specimen (+ 45°/-45°) | GPa (kN/mm²) | 4,12 |
| Impact strength printed specimen x-y (+ 45°/-45°)(Charpy) | kJ/m² | 35 |
| Shore hardness | --- | -- |
Thermal properties
| Glass transition temp. | °C | 87 |
| Heat distortion temp.(HDT) | °C | 90 |
Data Sheets
Printers
The Material has been tested on following printers:
| Printer | F3 PA-CF Pro | F3 PA-GF Pro | F3 PA Pure Pro | F3 PA-CF Lite | F3 PA Pure Pro |
| 3NTR A2/A4 | x | x | x | x | x |
| Evo-Tech Evolizer EL-102 | x | x | x | x | x |
| Hage3D 84L/140L | x | x | x | x | x |
| Multec M500/M800 | x | x | x | x | x |
| Prusa I3 MK3S | x | x | x | ||
| Raise3D N2/N2+ (Bondtech-upgrade) | x | x | x | x | x |
| Raise3D Pro2/Pro2+ | x | x | x | ||
| Ultimaker S5/S3 | x | x | x | x | x |
| Zortrax M200 Plus | x | x |